Butadiene-α-methylstyrene block – copolymer – a thermoplastic elastomer (TPE-R DMST) occupies a special place among the ethylene – vinyl aromatic block copolymers. TPE-R DMST comprising as plastic – poly-α-methylstyrene unit and elastic – polybutadiene block. TPE-R DMST has high heat resistance, flexibility, abrasion resistance compared to butadiene-styrene thermoplastic elastomer (TPE DST). The synthesis of block copolymers of butadiene and α-methylstyrene was carried out. The process of polymerization the α-methylstyrene characterized the high speed of polymerization in polar medium and low reaction speed in hydrocarbon solvents. Anionic catalyst nbutyllithium (n-BuLi) and high concentration – 60–80% α-methylstyrene in the mixture influenced by synthesis of the 1st block of TPE-R DMST, it’s technologically difficult. Found that the low temperature of polymerization α-methylstyrene (+61 o C), the reversibility of these reactions and the high concentration of residual monomer are very importance. It was revealed that a high polymerization rate α-methylstyrene can be achieved by conducting the reaction in a hydrocarbon solvent with polar additives compounds such as tetrahydrofuran (THF) and methyl tert-butyl ether (MTBE). The conditions for the synthesis of P-DMST were developed. The kinetics of polymerization for the first DMST-P unit was obtained. Analysis of physical and mechanical properties DMST-P samples was conducted. The optimum content of bound α-methylstyrene block copolymer provides a good combination of properties in a relatively wide temperature range. The tensile strength at normal and elevated temperatures, the hardness and the stiffness of the polymer increased by increasing the content of bound α-methylstyrene. The elongation and the elasticity reduced by increasing the content of bound α-methylstyrene.

thermoplastic elastomer, α-methylstyrene, n-butyllithium, tetrahydrofuran, methyl tertiary butyl ether, tetraethoxysilane, cyclohexane, melt index

1. Imanov A., Mukhtar S., Sarsenbaeva A., Nurkenov N. et al. Sposob polucheniya termoelastoplastov [Method for producing thermoplastic elastomers] Patent KZ, no. WO/2014/142637, 2014. (in Russian)

2. De Rosa C., Auriemma F. Single site metalorganic polymerization catalysis as a method to probe the properties of polyolefins. Polymer chemistry, 2011, vol. 2, no. 10, pp. 2155–2168. DOI: 10.1039/c1py00129a

3. Akhmetov I.G., Boreyko N.P., Bourganov R.T., GluchovskoiV.S. et al. Kinetic parameters of “lithium” polybutadiene polymerization and its molecular characteristics – the influence of toluene and hexane-1 concentration. Kauchuk I rezina. [Rubber], 2010, no. 3, pp.2–4. (in Russian).

4. Akhunova R.R., Biglova R.Z., Talipov R.F., Tsadkin M.A. et al. A modifying additive to road bitumen. Elektronnyi nauchnyi zhurnal neftegazovoe delo. [Electronic science journal of the oil and gas business], 2013, no. 2, pp. 359–369. (in Russian).

5. Podkopaeva S.V., Кhromykh E.A. Justification of the choice of the technological mode of production of butadiene-styrene thermoplastic elastomer. Promyshlennoe proizvodstvo i is-pol'zovanie elastomerov. [Indusrtrial production and use of elastomers], 2014, no. 2, pp. 28–30. (in Russian)